连福全

[1]

，蔡劲树

摘  要

：为了得到耐候性极好、高性价比的聚酯改性氟碳粉末涂料，本文使用高压静电喷涂制备涂膜，并通过测试粉末涂料的粒径、涂膜表面张力、粉末振实密度以及不同类型流动助剂来探究其对聚酯改性氟碳粉末耐候性能的影响。

关键词

：氟碳粉末涂料；粒径；表面张力；流动助剂；耐候性。

The exploration of Weatherability for Polyester

Modified Fluorocarbon Powder

Lian Fuquan, Cai Jinshu

(Guangdong Huajiang Powder Technology Co., Ltd., Zhaoqing, Guangdong 526238)

Abstract

:The objective of this study was to explore the influence of the particle size, surface tension of the coating film, powder tap density and different types of flow promoters on the weatherability of polyester modified fluorocarbon powders by exploring the coating film prepared by high-voltage electrostatic spraying to get excellent weatherability and cost-effective fluorocarbon-modified polyester powder coating.

Keywords

: Fluorocarbon powder coating; Particle size; Surface tension; Flow promoter; Weatherability.

前言

氟碳粉末涂料分成热固型和热塑型，本文所制备聚酯改性氟碳粉末为热固性粉末涂料。和普通溶剂型涂料及水性涂料不同，热固型粉末涂料的分散介质不是溶剂和水，而是空气。它具有无溶剂污染，100%成膜，能耗低的特点。随着粉末涂料的发展以及人们对粉末涂料的认识，不同功能型的粉末涂料越来越多，其中耐候性能一直都是粉末涂料的主要关注点。而氟碳粉末的耐候性能在所有的粉末涂料中是最好的，因为氟树脂分子中的化学键C-F键能非常大，其分子键非常稳定，能有效抵抗紫外线对它的破坏

[1]

。

纯氟碳粉末涂料因为其本身的耐候性优势备受欢迎，但是纯氟碳粉末涂料的机械性能比较差、价格昂贵，在市场中很难推广开来，改性氟碳粉在这种情况下应运而生。改性氟碳粉既能满足客户对耐候的需求，又降低了生产商的成本，是目前比较理想的超耐候粉末涂料。改性氟碳粉一般有聚酯改性氟碳粉、聚氨酯改性氟碳粉、丙烯酸改性氟碳粉。本文选择聚酯改性氟碳粉来做测试，聚酯改性氟碳粉是通过一定的质量比将聚酯粉末与纯氟碳粉末均匀混合制成的。本文通过探究聚酯改性氟碳粉末两个组份的粒径、涂膜表面张力、粉末振实密度以及外加流动助剂对聚酯改性氟碳粉末耐候性的影响。

1实验部分

1.1主要原材料

普通耐候聚酯树脂A（市售），氟树脂B（市售），氟树脂C（市售），封闭型异氰酸酯B-1530，三缩水甘油异氰尿酸酯TGIC，流平剂（南海奉化），光亮剂（南海奉化），脱气剂（南海奉化），纳米SiO

2

（市售），氧化铝C（Al

2

O

3

•C，市售），其他助剂、颜填料。

1.2测试项目及仪器设备

1.3实验配方及粉末涂料制备

与其他热固性粉末涂料制备方法一样，将基料按配方称重，混合均匀，通过挤出机熔融....